A low-C 5-Mn ultra-heavy plate steel with high microstructural homogeneity and excellent strengthtoughness combination
..

Journal of Material Sciences & Engineering

ISSN: 2169-0022

Open Access

A low-C 5-Mn ultra-heavy plate steel with high microstructural homogeneity and excellent strengthtoughness combination


6th International Conference and Exhibition on Materials Science and Engineering

September 12-14, 2016 Atlanta, USA

Jun Hu, Lin-Xiu Du, Hong-Yan Wu, Hao Liu and Cai-Ru Gao

Jun Hu, Lin-Xiu Du, Hong-Yan Wu, Hao Liu and Cai-Ru Gao

Scientific Tracks Abstracts: J Material Sci Eng

Abstract :

Ultra-low carbon 5Mn steel was subjected to control rolling and direct cooling, and then the ultra heavy plate steel of 100 mm thickness was intercritically tempered at 650�ºC. The microstructure consisted of alternative laminate structure of tempered martensite and reversed transformed austenite. The yield strength, tensile strength, and elongation of 638 MPa, 805 MPa, and 34%, was obtained in the 1/2 thickness of the plate, and 670 MPa, 818 MPa, and 32% in the 1/4 thickness. Moreover, the impact absorbed energy tested at -80�ºC was higher than 100 J. The high microstructure and mechanical properties homogeneity along thickness was obtained because 5Mn alloying significantly increase the hardenability of the ultra-thick plate steel. The partitioning of Mn from tempered martensite to austenite greatly enhanced the stability of reversed austenite. Austenite transformed to martensite under tensile straining, and the volume fraction decreased gradually. The TRIP effect of metastable reversed transformed austenite played the significant role on improving toughness and plasticity.

Biography :

Jun Hu has completed his PhD from The State Key Laboratory of Rolling and Automation, Northeastern University. He is dedicated to study the microstructural evolution and mechanical properties control of advanced high strength steel. He has published more than 20 papers in the SCI indexed journals.

Email: wuhy@ral.neu.edu.cn

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward