| Author |
Nr. specimens |
Material |
Results |
| Belli et al. [47] |
10 |
5 ceramic
5 composite |
Equivalent fatigue strength
degradation at lods 0.56 in |
| Beatriz et al. [48] |
70 |
Vitadur Alpha
Ceramic
Different cements |
Showed lower fracture resistance |
| Suzuki et al. [49] |
7 |
Indirect compos.
(2 photo, 5 photo/heat) |
Wear resistance similar to type III gold alloy tested |
| Magne P et al. |
14 onlay |
Paradigm MZ100
e-max CAD &MarkII |
Survival rate 36%. Failure at av. load 157N & 123N |
| Morito S et al. [50] |
30 maxillary premolars |
Ceramic
Composite |
Fracture ceramic/composite similar to impact teeth.
57% greater ability to absorb impacts than ceramic |