material

the form of material

sample size

cell dencity
(cells/cm2)

n

days in culture

technical problems

results /
conclusions

cell survival

polylactide

membrane

ø 15 mm

275000-300000

11

2-12

-

too stiff material

++

chitosan

membrane

ø 15 mm

275000-350000

13

2-12

immunocytochemistry: background

the cells survived but did not attach as well as on controls

++

chitosan

gel

nd

nd

nd

nd

gelation

the cells did not spread

-

POC

membrane

ø 13 mm

300000-400000

2 (POC, POC on CNT), 3 (CNT on POC)

6-7

LIVE/DEAD: background

the cells survived but there were not as much cells as on controls

-

PEOT/PBT

membrane

ø 20 mm, thickness 90-130 µm

335000-414000

3 (1000 g/mol), 4 (300 g/mol)

6

-

the cells survived but there were not as much cells as on controls

-

PuraMatrix™

gel

250 µl in 24 well plate

300000-400000

10 (*)

4-9

uneven gelling, the gels detached

the cells did not migrate inside the gel

+

collagen

gel from commercial

250-500 µl in 24 well plate

331500-350000

10 (**)

nd

the gels detached

the cells were not evenly spread

+

collagen

gel from self isolated

250 µl in 24 well plate

400000 (on) / 1400000 (in)

14 (***)

4-10

-

the cells were evenly spread and migrated inside the gel

+++

POC = Poly(1,8-octanediol-co-citric acid), CNT = carbon nano tube, PEOT = poly(ethylene oxide terephtalate), PBT = poly(butylene terephtalate) (*) gel concentration = 0,15-0,4 %; (**) gel concentration = 0,784-1,960 mg/ml; (***) gel concentration = 0,8384 mg/ml
Table 1: The biomaterials used in the study. Summarizing table of detailed information about the experiments with different biomaterials.