| Illumination
(mW cm−2 ) |
Electrolyte
support |
Jsc(mA cm−2 ) |
Voc (V) |
FF |
Efficiency (%) |
| 100 |
None |
12.30±0.12b |
0.76±0.01 |
0.57±0.03 |
5.34±0.36 |
| 100 |
0.2mm PC film |
11.470.31 |
0.76±0.02 |
0.49±0.04 |
4.29±0.39 |
| 100 |
0.05mm PC film |
7.84±0.92 |
0.76±0.01 |
0.54±0.03 |
3.17±0.40 |
| 50 |
None |
5.78±0.13 |
0.72±0.01 |
0.61±0.02 |
5.18±0.18 |
| 50 |
0.2mm PC film |
5.64 |
0.73 |
0.58 |
4.70 |
| 50 |
0.05mm PC film |
4.30±0.50 |
0.71±0.01 |
0.70±0.04 |
4.25±0.51 |
| 20 |
None |
0.77±0.05 |
0.64±0.01 |
0.63±0.01 |
1.62±0.15 |
| 20 |
0.2mm PC film |
0.84 |
0.66 |
0.69 |
1.89 |
| 20 |
0.05mm PC film |
0.67±0.27 |
0.64±0.01 |
0.84±0.02 |
1.34±0.22 |
a Single-sealed cells with active area of 0.28 cm2; electrolyte consisting of 0.8M PMII/0.05M I2/0.5M NMBI in MPN.
b Mean ± standard deviation (N=3) except for 0.2 m PC film at 20 and 50 mW cm-2.
|