Department of Biotechnology, Faculty of Life Sciences and Informatics, Balochistan University of Information Technology, Engineering and Management Sciences, (BUITEMS), Quetta, Pakistan
Received date: September 19, 2016; Accepted date: December 12, 2016; Published date: December 15, 2016
Citation: Khan NT, Jameel J, Rehman SUA (2016) Biogenesis of Silver Nanoparticles Using Penicillium fellutanum and Determination of its Antibacterial Activity. Biochem Anal Biochem 5:305. doi: 10.4172/2161-1009.1000305
Copyright: © 2016 Khan NT, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Visit for more related articles at Biochemistry & Analytical Biochemistry
Silver nanoparticles were produced from cell free extract of Penicillium fellutanum with aqueous silver nitrate. The synthesized silver nanoparticles were produced in colloidal form outside the fungal cell in the external yeast malt extract (YM) media. Visual change in the color of the extract from deep yellow to grey indicates bioreduction of silver metal ions resulting in silver nanoaprticles synthesis. The reaction mixture was characterized by UV-visible spectrometry and absorption was measured from 350 nm to 450 nm and λ-max was found to be 430 nm. Antibacterial efficacy of AgNPs was investigated using disc diffusion method against the bacteria Staphylococcus aureus, Escherichia coli, Aeromonas hydrophila and Klebsiella pneumoniae and was found to be effective antibacterial agent. Thus Penicillium fellutanum could be used as a source of silver nanoparticles, an ecofriendly alternative process for the mycosynthesis of stable AgNPs with future applications in biomedical based on its antibacterial properties.
Penicillium fellutanum; AgNPs; Yeast malt extract; BUITEMS
In recent years nanoparticles have been produced by industries for commercial application having many benefits. Biosynthesis of nanoparticles attracts many researchers and industries to explore microorganisms as the perfect biological system for the production of different nanoparticles. The metabolic activity of these microorganisms enables the extra cellular or intracellular synthesis of nanoparticles utilizing different mode of synthesis [1-4]. Microorganisms possess the capability to minimize the toxicity of the metal ions through bioreduction or by the formation of insoluble complexes with metal ion in the form of colloidal particles. According to Vijayaraghavan and Nalini, in comparison, biologically synthesized nanoparticles have proved to be better than the chemically synthesized ones due to a better control over the crystal growth because of slower kinetics which reduces the overall investment involved in nanoparticle synthesis . Not only reduction in the overall cost makes it less expensive process but also it is an environmental friendly method because it does not involve the use of toxic chemicals that are expensive and harmful for the environment as used in non-biological synthetic procedures for the synthesis of nanoparticles of poor morphology. Therefore nanoparticles of distinct morphology can be obtained through the optimization of culture conditions using biological organisms. In present work AgNPs were fabricated using Penicillium fellutanum extract incubated with silver nitrate solution and its antibacterial activity was tested against various pathogenic bacteria.
Fungal biomass production
Penicillium fellutanum was isolated from soil and cultured was grown in 1L yeast malt extract (YM) broth media which consists of glucose (10 g), malt extract (3 g), peptone (5 g) and yeast extract (3 g) dissolved in 1000 ml of distilled water. The culture medium was autoclaved for 15 min at 121°C at 15 psi (pound/square inches). The media was inoculated with Penicillium fellutanum culture in sterile air under Laminar flow cabinet by the help of sterilized wire loop. Incubation of the cultured flasks on a rotatory shaker at 150 rpm for 72 hours was done at room temperature.
Penicillium fellutanum live cell filtrate
Penicillium fellutanum mycelia were filtered using Whatman’s filter paper no.42 after 72 hours of incubation. The obtained live cell filtrate was further filtered through polyvinylidene fluoride (PVDF) membrane to obtain cell free fungal extract. The filtrate was then centrifuged at 10000 rpm for 20 min.
Biogenesis of silver nanoparticles
10 ml cell free fungal extract was than incubated with 90 ml of 1 mM AgNO3 in the dark to nullify any photochemical reaction at 25°C for 48 hrs. The change in color of the experimental flask containing fungal filtrate incubated with AgNO3 results in the formation of AgNPs. Control containing freshly prepared YM media with aqueous silver nitrate was run simultaneously with the experimental flasks. Experiment and control were performed in triplicates.
Confirmation of silver nanoparticles
The reaction mixture was characterized by UV visible spectrometry (JENWAY 6305) and absorption was measured from 350 nm to 450 nm to determine λ max.
Antibacterial efficacy of AgNPs was investigated against the bacteria Staphylococcus aureus, Escherichia coli, Aeromonas hydrophila and Klebsiella pneumoniae on YM agar plates (agar (20 g), glucose (10 g), malt extract (3 g), peptone (5 g) and yeast extract (3 g)) dissolved in 1000 ml of distilled water by disc diffusion method. The culture medium was autoclaved for 15 min at 121°C, 15 psi (pound/square inches). Before pouring 0.5 ml antibiotic ampicillin was added to the medium to inhibit bacterial contamination and 1 ml of 10% sterilized tartaric acid solution to adjust pH of media (4.2-4.5). The surface of the agar was inoculated with the test pathogens. Then sterile discs of size one centimeter were prepared and placed on agar surface impregnated with 40 μL silver nanoparticle solution. Incubation was done at 37°C for 48 hrs. Calliper was used to measure the diameter of the inhibition zone. Silver nitrate solution impregnated discs were used as control.
Bioreduction of silver metal ions were observed by a gradual change in the color of the experimental flask from deep yellow to grey is due to the excitation of plasmon vibrations with AgNPs and the absorbance maximum absorbance was observed at 430 nm as shown by the UV-Visible spectra [6,7] (Figure 1). UVvisible spectra clearly indicates a single peak depicting synthesis of spherical shaped AgNPs with uniform distribution and no aggregation of the nanoparticles were observed [8-10].
The mechanistic aspect behind the invitro synthesis of AgNPs under standard lab conditions was not known until it was hypothesized later that reduction of silver metal ions was carried out by NADPH dependant enzyme nitrate reductase which forms its corresponding AgNPs. Antibacterial efficacy of AgNPs was tested against bacteria including Staphylococcus aureus, Escherichia coli, Aeromonas hydrophila and Klebsiella pneumoniae  and diameter of the inhibition zone was measured in centimeters (Table 1).
|S.no||Test pathogens||Zone of inhibition (cm)
Table 1: Anti-bacterial efficacy of AgNPs.
AgNPs synthesized from Penicillium fellutanum filtrate showed enhanced antibacterial effect against E. coli, Aeromonas hydrophila and Staphylococcus aureus as the measured diameter of the inhibition zone was found to be 1 cm, 0.9 cm and 0.9 cm respectively. However moderate antibacterial effect was seen against Klebsiella pneumoniae. The mechanism of inhibition is still unknown but the possible proposed assumption is the ionic binding of AgNPs to the surface of the bacterial cell or by means of AgNPs binding to the thiol group of the enzymes [12,13].
Biosynthetic approach for silver nanoparticle synthesis is a novel approach using fungi as the biological organism. For example Penicillium fellutanum could be used as a source of silver nanoparticles, an ecofriendly alternative process for the mycosynthesis of stable AgNPs with enhanced antibacterial activity. However, studying the novel shape and size dependent physical and chemical properties of nanoparticles and their subsequent interaction could help in understanding its antibacterial mechanism and will lead to the development of a new range of antibacterial agents with widespread clinical applications.
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals