alexa In Vitro Study for Comparing the Cytotoxicity of Silver and Gold Nanospheres on Raw 264.7 Murine Macrophage Cell Line | Open Access Journals
ISSN: 2155-9597
Journal of Bacteriology & Parasitology
Like us on:
Make the best use of Scientific Research and information from our 700+ peer reviewed, Open Access Journals that operates with the help of 50,000+ Editorial Board Members and esteemed reviewers and 1000+ Scientific associations in Medical, Clinical, Pharmaceutical, Engineering, Technology and Management Fields.
Meet Inspiring Speakers and Experts at our 3000+ Global Conferenceseries Events with over 600+ Conferences, 1200+ Symposiums and 1200+ Workshops on
Medical, Pharma, Engineering, Science, Technology and Business

In Vitro Study for Comparing the Cytotoxicity of Silver and Gold Nanospheres on Raw 264.7 Murine Macrophage Cell Line

Hala Ragab Khalil Ali1*, Moawad MS2 and Selim SA3

1Department of Microbiology and Immunology, Animal Health Research Institute (AHRI), Dokki, Egypt

2Faculty of Veterinary Medicine, Department of Toxicology and Forensic Medicine, Giza, Egypt

3Faculty of Veterinary Medicine, Department of Microbiology and Immunology, Giza, Egypt

*Corresponding Author:
Ali HRK
Department of Microbiology and Immunology
Animal Health Research Institute (AHRI), Dokki, Egypt
Tel: +20 33374856
E-mail: [email protected]

Received Date: January 28, 2016 Accepted Date: February 27, 2016 Published Date: March 02, 2016

Citation: Ali HRK, Moawad MS, Selim SA (2016) In Vitro Study for Comparing the Cytotoxicity of Silver and Gold Nanospheres on Raw 264.7 Murine Macrophage Cell Line. J Bacteriol Parasitol 7:264. doi: 10.4172/2155-9597.1000264

Copyright: © 2016 Ali HRK, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.

Visit for more related articles at Journal of Bacteriology & Parasitology

Abstract

Silver nanospheres (AgNSs) and gold nanospheres (AuNSs) made a huge commercial and scientific interests due to their antimicrobials potency, use in nanomedicine and drug delivery systems. Macrophages are the primary site for clearing waste substances from tissues and the intracellular infections produced by pathogens like Mycobacterium tuberculosis. Therefore, studying the cytotoxic effects of nanomaterials on such promising model will open new era towards safe use of nanobased treatments of intracellular pathogens. In This study, the effect of three different concentrations (10, 20, 40 μg/ml) of AuNSs and AgNSs with an average diameter of 20 nm was studied on RAW264.7 murine macrophage viability for 3 hours using XTT assay. AuNSs were found nontoxic to macrophages at all tested concentration. However AgNSs showed acute decline in viability of RAW264.7 cells even at the lowest concentration (10 μg/ml). In another experiment, the effect of AuNSs and AgNSs was examined on short and long term manners by treating macrophages with single dose of 20 μg/ml for different time points (0, 10, 20, 30, 60 minutes, 24, and 48 hours). Results revealed that AgNSs induced acute cytotoxicity to macrophages till 48 hours, while gold nanospheres were safe to RAW264.7 cells at all-time points compared to untreated control. Thus the AuNSs might represent a safe drug delivery platform for combating the intracellular pathogens like M. tuberculosis without hurting their host cells.

Keywords

AgNSs; AuNSs; XTT

Introduction

Recently, nanoparticles opened a broad area of interest due to their unique physical and chemical properties. They became a successful platform in a long list of useful applications including biomedicine, chemistry, food industry, cosmetics and electronics. The metal nanoparticles played the back-bone role in many medical and manufacturing industries, while silver and gold nanoparticles were of utmost interest among all metal-based nanomaterials due to their incorporation in different products. Gold nanoparticles has been attracted great interest in diagnostic and therapeutic applications, especially cancer therapy and drug delivery [1,2]. On the other hand, silver nanoparticles were widely incorporated in many applications such as food packaging [3], wound dressing and surgical instruments [4,5], water purification [6], and textiles [7]. Many authors have addressed the potential use of silver nanoparticles as a vehicles for antimicrobial agent [8,9], while others reported the bactericidal effect of AgNPs on gram negative bacteria [10] as well gram-positive and intracellular infections [11]. The macrophages are the primary host infected by intracellular pathogens, like Mycobacterium tuberculosis (TB) and Brucella , which significantly constitute public health concerns. Unusually and professionally, these infecting intracellular pathogens can evade the hostile environment of macrophage, block the maturation of phagosome into phagolysosome, survive, and multiply inside the infected macrophages. Moreover, disease control and treatment of these pathogens became a difficult challenge due to their intracellular survival nature, and the emergence of new drug-resistant bacterial strains. Furthermore, macrophages are among the most important cellular components of innate immunity, and they are considered the main resident phagocytic cells inside all organs for clearance of any waste material in blood circulation and tissues. Not even, these cells were found to have higher capacity to internalize nanomaterials more efficiently than any other cellular types in the body [12]. So developing a nano-based drug delivery system, with high ability to target macrophages and deliver the carried antibacterial drugs inside their infected cells, could be a promising approach for fighting these pathogens and curing their caused chronic diseases. Nano-based drug delivery systems have attracted the attention of many research groups, which concluded that metal nanoparticles as gold and silver could be promising noble nanomaterials in biomedicine and drug delivery [13-15]. However the gold and silver nanoparticles have shown antimicrobial activities against Gram-negative and Grampositive bacteria [16,17], they revealed antimycobacterial activities against extracellular TB [18]. Other different nanoparticles were investigated in vitro and in vivo as drug delivery vehicle for anti-TB drugs. Kisich et al. used biodegradable nanopolymers and enhanced the efficacy of encapsulated moxifloxacin against the intracellular Mycobacterium tuberculosis infection [19], Pandey and Khuller used the liposomal nanoparticles [20], while Clemen et al. targeted M. tuberculosis infected macrophages through functionalized mesoperous silica nanoparticles [12]. Consequently we assume that testing silver and gold nanoparticles as drug delivery vehicle and loading them with anti-TB drugs in an attempt to target the M. tuberculosis infected macrophages may potentiate their efficacy against the intracellular TB infection. Although the nano-based drug delivery systems offer a potential advantage in accumulating drug targets inside the macrophage and reducing the systemic side effects, nanoparticles have a high binding capacity to biological molecules and can access into the mammalian tissues and cells easily. These characteristics may possibly generate adverse side effects to mammalian cells and may result in significant toxicities even if they are biochemically inert at bulk size. Thus saftey of the employed drug delivery vehicle to the infected host macrophage cells must be well tested, because if the nanoparticles were cytotoxic, the host cells will be killed and liberate the intracellular pathogens which in turn attack and infect other healthy macrophages and spread the disease rather than control and treat. From this view, RAW264.7 murine macrophage cell line was selected, as ideally suited cell model, and two metal nanoparticles, gold and silver were employed as nano-based drug delivery systems; maintaining the same physical and chemical properties as shape, size, and capping material. The aim of this study is to assess dose-dependent and time-dependent cytotoxicity of silver and gold nanospheres on RAW264.7 murine macrophage cell line using the cell viability assay (XTT) and microscopical examination. Since a current deficient knowledge of nanosized silver and gold cytotoxicity exist on RAW264.7 macrophage cells. Thus in the future, this study could contribute to scientific community, improving the selection of suitable drug delivery systems comparing between the silver and gold nanospheres, which currently are the two best options.

Materials and Methods

All chemicals were analytically pure grade from Sigma-Aldrich (St. Louis, USA). All cell culture media and reagents were from Mediatech (Tewksbury, MA, USA), while the cell scraper 18 cm handle/1.8 cm blade used for sub culturing cells was from Falcon (Wiesbaden, Germany). XTT cell viability kit (Catalog number: 30007) used for cytotoxicity studies was purchased from Biotium (Hayward, CA, USA).

Synthesis of gold nanospheres

Citrated gold nanospheres (AuNSs) with an average diameter of 20 nm were synthesized as described by Frens [21] by the reduction of chloroauric acid with trisodium citrate. Briefly, 5 mL of 5 mM HAuCl4. 3H2O were added to 90 mL of deionized water (DI) and heated with continuous stirring until it began to boil. five mL of 0.5% trisodium citrate solution were added with continuous heating and stirring until the solution turned into wine red color, then it was kept to cool at room temperature before characterization.

Synthesis of silver nanospheres

Silver nanoparticles were synthesized by chemical reduction method as reported by Turkevich et al. [22]. Briefly, a solution of AgNO3 was used as Ag1+ ions precursor, while sodium citrate as mild reducing agent and Polyvinyl Alcohol (PVA) played the role as stabilizing agent. The color of the solution slowly turned into greyish yellow indicating the reduction of the Ag1+ ions into silver nanoparticles.

Characterization of synthesized nanoparticles

The size and shape of synthesized gold nanoparticles were characterized using transmission electron microscopy (TEM; JEOL 100CX-II, Tokyo, Japan) and UV-Vis spectrophotometer. The average particle diameters of synthesized nanoparticles were measured by processing TEM images using ImageJ software (National Institute of Health NIH, Bethesda, MA, USA). Briefly, a drop of synthesized nanoparticles solutions was placed on carbon coated TEM copper grid and allowed to dry for 5 minutes, and then the excess solution was removed using a blotting paper. The copper grid was inserted in TEM microscope and nanoparticles images were captured for further analysis with ImageJ software. The surface plasmon resonance peaks were detected using UV-Vis spectroscopy at 520 nm for gold nanospheres and 420 nm for silver nanospheres.

Macrophage cell culture

The murine macrophage, RAW264.7 cell line were cultured in Dulbecco's Modification of Eagle's Medium (DMEM) supplemented with 4.5 g/L glucose, L-glutamine, and sodium pyruvate, 10% fetal bovine serum, and 1% streptomycin/penicillin antibiotics. Cell cultures were kept at 37°C in a humidified 5% CO2 incubator, and when confluency reached 70%, cells were scraped with cell scraper 18 cm handle /1.8 cm blade and subcultured.

Microscopic examination

The cells were grown in 96 well plates at 1 x104 density per well for overnight, then treated with different concentration of AgNSs or AuNSs for fixed or different time points. The cell cultures were examined under inverted microscope (Olympus CKX41, Tokyo, Japan) using 10x or 40x objectives, while images of cells were captured using Samsung digital camera.

Cellular viability

To determine the effect of different concentration of AuNSs and AgNSs on RAW264.7, cells were seeded in 96 well plates at an approximate density of 1x 104 cells per well for 24 h. After 1 day, the old media was removed and replaced with new DMEM media contained 10, 20, 40 μg/ml of gold or silver nanospheres. In another experiment, the cytotoxicity of murine macrophage RAW 264.7 cells were tested after their exposure to fixed dose of 20 μg/ml gold or silver nanospheres for different short and long term time points (0, 10, 20, 30, 60 min, 24, and 48 h). After incubation for different time points, the culture media contained nanoparticles was replaced with clear DMEM without phenol red (CDMEM) contained the XTT solution and incubated for overnight. After incubation, the intensity of color was measured as absorbance at 450 nm and 690 nm for gold and silver nanospheres consequently using Synergy H4 Multimode Plate Reader (Biotek,Winooski, VT, USA). The viability percent was compared to untreated control cells as a result of three independent experiments.

Statistical analysis

The obtained viability of RAW cells treated with NPs was compared to untreated controls using unpaired t-tests, Results are expressed as the mean ± SE of three independent experiments. The differences between the cell viability studied were not found to be statistically significant. The level of significance was set at P<0.05.

Results

The gold and silver nanospheres were successfully synthesized. And upon characterization AuNSs revealed significant plasmon resonance peak at 520 nm while the peak of silver nanoparticles was detected at 420 nm (Data not shown). Transmission electron microscope (TEM) confirmed and revealed the monodispersity of the synthesized nanoparticles with an average particle diameter of 20 nm for both gold and silver nanospheres (Figure 1). As the first and the most determinative effect following exposure of cell monolayer to toxic agent is the morphological alterations in the cell shape, therefore we used the optical microscope to determine cellular damage and thus, to establish an index of cytotoxicity in the model used. In a pilot experiment, RAW264.7 cells were exposed to 40 μg/ml of either Au or AgNSs for 3 h using light microscopical examination, the macrophages were severly damaged upon exposure to AgNSs and their morphology and shape significantly impaired. In contrast cells exposed to gold nanospheres were almost intact with higher viability appearance compared to cells exposed to silver nanospheres (Figure 2). For confirming the cytotoxic effect of silver nanospheres on RAW264.7 morphology, a main experiment was designed in order to include more geometrical time points and to quantify the viability result using the XTT assay. Different triplicates of RAW264.7 macrophages cells were treated for 3 h with three different concentrations 10, 20 & 40 μg/ml of negatively charged citrated AgNSs and in comparison to AuNSs. After incubation time the results revealed a significant acute cytotoxicity and decline in the viability percentage of the treated cells with all the three concentrations of AgNSs (10, 20 & 40 μg/ml) (Figure 3a and Table 1). Surprisingly, the RAW 264.7 incubated with the same concentrations of gold nanospheres showed much better viability as illustrated in figure 3b and shown in table 1. In order to examine the effect of short term and long term exposure of gold and silver nanoparticles on murine macrophage cells, the RAW264.7 cells were exposed to fixed dose of 20 μg/ml of either AuNSs or AgNSs for different time points (0, 10, 20, 30, 60 min, 24, and 48 h) and the cells were examined microscopically. The silver nanospheres had more significant alterations in cellular growth of RAW cells during first 20 minutes since more than 50% of cell populations lost their morphological integrity and characterized by shrinkage of their cell membrane. By the end of the hour about 25% of the cells were left in the plate wells. While after 48 hours there were no viable cells found in the microscopical field and the wells appeared empty except of some cells and lots of cell debris. On the other hand, gold nanospheres did not affect the morphology and viability of RAW264.7 cells at all tested time points. The treated cells appeared healthy without any cellular alterations in growth and looked viable with intact cellular membrane as shown in (Figure 4). The XTT assay was employed to quantify the viability of treated cells and as well to confirm the result obtained by the microscopical examination. The same experiment was repeated the cells exposed to 20 μg/ml of AuNSs or AgNSs for different time points up to 48 hours the viability declined but in severe manner than that recorded in their first hour of exposure to record 14.26 and 9.3% after 24 and 48 hours exposure respectively (Figure 5 and Table 2).

bacteriology-parasitology-gold-silver

Figure 1: TEM image of gold and silver nanospheres. A. TEM image of AuNSs showed an average particle size 20 nm and B. TEM image of AuNSs showed an average particle size 20 nm.

bacteriology-parasitology-severe-cell

Figure 2: Microscopical observation comparing between the cytotoxic effect produced by nanoparticles on Raw 264.7 cells at high concentration (40 μg/ml), A. illustrating no cytotoxic effect produced after 3 hours incubation with 40 μg/ml of AuNSs , B. AgNSs at the same concentration and the same exposure time result in severe cell death. (10X objective).

bacteriology-parasitology-severe-cell

Figure 3: Cell viability Data A. Cell viability results for the exposure of RAW264.7 cell line to three different concentrations (10, 20 & 40 μg/ml of AgNSs solutions for 3 hr). B. After exposure to AuNSs with the same three concentration Statistical significance has been indicated by ** (p-value<0.01), *** (p-value<0.001).

bacteriology-parasitology-gold-silver

Figure 4: The microscopic images of RAW264.7 cell line treated with 20 μg/ml of AgNSs or AuNSs for different time points (0, 10 min and 48 h). Upper: the RAW monolayer exposed to AgNSs at zero-time showing morphological alteration, after10 min almost all the cells looks shrinked and rounded and after 48 h. The field shows massive cell death and a lot of cell debris. Bottom: the RAW exposed to Au NSs for zero time , 10 min and 48 h are viable, healthy and showing no difference than untreated cells. NB (these images were taken by camera Samsung).

bacteriology-parasitology-cell-exposure

Figure 5: Viability results of RAW 264.7 cell exposure to 20 μg/ml AuNSs or AgNSs at different time points (0, 10, 20, 30 min, 1, 24 and 48 h). Statistical significance has been indicated by *** (pvalue< 0.001).

The concentrations Silver nanospheres Gold nanospheres
Viability% Viability%
Control 100 100
10 μg/ml 43 94.3
20 μg/ml 15.7 91.7
40 μg/ml 13.5 87.8

Table 1: The cell viability result of exposing raw macrophage cell line to three different concentrations of silver or gold nanospheres for fixed time (3 hrs).

The silver nanospheres exerted severe toxicity to RAW even at zerotime point as the viability percent recorded was 78% compared to the control. After 10 minutes the viability of cells were reduced to 63.3%, while after 20 and 30 minutes less than half of total number of cells/ wells were viable with viability percent 43 and 39.7%. By the end of first hour, viability of cells exposed to silver nanospheres was 24.9 which indicated that one quarter of the total cells per well were viable. The result indicated that raw cells were exposed to severe cytotoxicity upon their exposure to silver nanospheres of 20 μg/ml concentrations within one hour. Afterwards and up to 24 and 48 h. alternatively gold nanospheres did not exert a significant toxicity on murine macrophage even after long term exposure for 24 and 48 h. The cellular viability of cells exposed to 20 μg/ml of AuNSs was 92.2% and 86.8% after 24 and 48 h respectively (Figure 5 and Table 2).

Time points Silver nanospheres Gold nanospheres
Viability % Viability%
0 78 99.2
20 min 43.2 96.2
30 min 39.7 96.7
1 h 24.9 93.7
24 h 14.2 92.2
48 h 9.3 86.8

Table 2: Time exposure/ viability of raw macrophage exposed to fixed concentration (20 μg/ml) of silver or gold nanospheres for different time points.

Discussion

Taking together, the data of microscopical examination and viability assay revealed that silver nanospheres were highly toxic to RAW cell compared to their counterpart gold nanospheres at different concentration and time points. Up to our knowledge, these data might be the first results for comparing the cytotoxicity of silver and gold nanospheres on RAW 264.7 murine macrophage cell line. Haase et al. [23] showed that even the low doses of nano silver were highly toxic to human macrophage while treatment the cells with nanogold did not reveal significant toxicity even at higher concentration; the cells retained its viability up to 80% compared to control set. And Raymond et al. [24] studied the cytotoxicity of silver nanoparticles (20 nm and 110 nm) on different cell line including two murine primary alveolar macrophages (C57Bl/6, and MARCO), they concluded that the small size of silver nanoparticles (20 nm) was more toxic to all cell lines and more active with THP1 macrophage compared to larger sized silver nanoparticles (110 nm). In our current study, RAW264.7 macrophage cells were significantly and severly affected upon contact with silver nanospheres even at zero time with viability 78% compared to 99.2% with the counterpart gold nanospheres. Affected cells were shrinked and become more likely rounded. Arora et al. revealed that higher concentrations of AgNPs, the changed morphology of the cells attributed to the higher level of oxidative stress informs of decreased glutathione (GSH) and super oxide dismutase (SDS) and increased lipid peroxidation, which finally leads to apoptosis by increasing caspase-3 activity and DNA fragmentation [25]. Silver nanoparticles show moderate solubility and contribute silver ions upon contact with cell medium, so demonstrated cytotoxicity of silver nanospheres by microscopical examination and XTT assay might be due to the effect of instant action generated silver ions on the outer membrane of RAW 264.7 cells. The significant reduction of cellular viability at zero time point and the following 60 min as well the significant loss of cellular integrity under the microscope may support this assumption. Moreover, as nanoparticles internalization and accumulation inside the cells depend primarily on the incubation time with nanoparticles as stated by Trono et al. [26], the significant reduction of viability in cells exposed to AgNSs up to 10 minutes (63.3%) is likely due to possible action of silver nanoparticles and produced ions on the outer cellular membrane of RAW cells and not because of the possible AgNPs inside cells in this short term periods. This scenario supported by Beer et al. [27] who returned the toxic effect of AgNPs to the released ion mainly than cellular internalization. In contrast, the nanogold did not induce any toxicity upto the first hour of incubation with RAW cells and only induced slight reduction of the cellular viability after long term exposure up to 24 and 48 h. Further research investigations are needed to monitor the real time uptake of macrophages to different nanoparticles and detect the time and site of localization of the internalized nanoparticles as well the mechanisms of the action behind nanotoxicity of different nanoparticles to macrophages.

Conclusion

The gold nanospheres might be ideally suited as a safe drug delivery system especially for antimicrobial drugs against intracellular infections like M. tuberculosis (TB). They may selectively target the infected macrophages more efficiently and safely than silver nanoparticles. Our next research shall investigate the efficacy of gold nanoparticles as a drug delivery system for anti-tuberculosis drugs against intracellular TB infection. On the other hand, we will investigate the mechanism of action of silver nontoxicity on macrophages through real time monitoring of their uptake and intracellular localization.

Acknowledgements

The authors acknowledge Prof. Dr. Rafeek Soliman from Microbiology and Immunology Department for permission to use his tissue culture unit and all its facilities. As well, authors acknowledge Science and Technology Development Fund (STDF; Cairo, Egypt) for the financial support of this study.

References

Select your language of interest to view the total content in your interested language
Post your comment

Share This Article

Relevant Topics

Recommended Conferences

Article Usage

  • Total views: 8114
  • [From(publication date):
    April-2016 - Jul 22, 2017]
  • Breakdown by view type
  • HTML page views : 7991
  • PDF downloads :123
 

Post your comment

captcha   Reload  Can't read the image? click here to refresh

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords