Research Article

Effect of HF Welding Process Parameters and Post Heat Treatment in the Development of Micro Alloyed HSLA Steel Tubes for Torsional Applications

Udhayakumar T* and Mani E

Corporate Technology Centre, Tube Investments of India Ltd, Chennai-600 054, India

*Corresponding Author:
Udhayakumar T
Corporate Technology Centre
Tube Investments of India Ltd
Chennai-600 054, India
Tel: +91-44-42291950
E-mail: [email protected]

Received Date: April 07, 2017; Accepted Date: April 24, 2017; Published Date: April 29, 2017

Citation: Udhayakumar T, Mani E (2017) Effect of HF Welding Process Parameters and Post Heat Treatment in the Development of Micro Alloyed HSLA Steel Tubes for Torsional Applications. J Material Sci Eng 6: 334. doi: 10.4172/2169-0022.1000334

Copyright: © 2017 Udhayakumar T, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.

 

Abstract

The aim of the present study is to investigate the effect of High frequency (HF) Electric resistance welding process parameters and post heat treatment on the torsional fatigue life of micro alloyed HSLA steel tubes. Micro alloyed grades exhibit higher strength and formability owing to the presence of fine recrystallized ferritic grains due to thermo mechanical treatment and presence of alloying elements like Vanadium, Niobium and Titanium. Welded tubular components made of micro alloyed HSLA steel grades are highly emerging and manufacturing them remains quite challenging. Weld bond width, HAZ width and bond angle are the significant factors that directly influences the Weld quality and strength. The effect of key welding parameters like Heat input, welding temperature, squeeze roll pressure, Vee-angle, Vee-length and Impeder diameter on the above mentioned significant factors was analysed. Narrow bond, Minimum HAZ width with pronounced Hour glass pattern and optimum bond angle resulted in superior bond strength and formability of HSLA tubes. Microstructural characterization of the samples was carried out using Light optical microscopy and Scanning electron microscopy. Residual stress was determined using X-ray diffract meter and tube slitting method. Higher tensile residual stress of magnitude 200 MPa was observed in the weld region. Since such high magnitude of tensile residual stress is detrimental to torsional fatigue life, stress relieving of the tubes was carried out at different subcritical temperatures 650°C and 700°C with soaking time of 45 minutes. Without significant drop in the tensile properties, compressive residual stress of magnitude 129 MPa was observed at a particular stress relieving cycle. As an effect of stress relieving heat treatment below Ac1 temperature, there is a significant improvement in the Torsional fatigue life of the HSLA steel. Thus, High Frequency welded micro alloyed HSLA steel tubes with enhanced torsional fatigue performance were successfully developed.

Keywords

Share This Page

Additional Info

Loading
Loading Please wait..
 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords