Dissimilar welding of high shear strength Ti2SnC/Cu/Ti6Al4V joint at low temperature
..

Journal of Material Sciences & Engineering

ISSN: 2169-0022

Open Access

Dissimilar welding of high shear strength Ti2SnC/Cu/Ti6Al4V joint at low temperature


2nd International Conference and Expo on Ceramics & Composite Materials

July 25-26, 2016 Berlin, Germany

Wenbo Yu, Kai Zhu and Xiong Shoumei

Tsinghua University School of Material Science and Engineering, China

Scientific Tracks Abstracts: J Material Sci Eng

Abstract :

In this work, as the biotoxicity of vanadium element in TC4 has limited it biomedical applications. Recently, nanolaminate ternary MAX phases (M for early transition metal, A for A-group element, and X for either carbon or nitrogen), combining metal-like and ceramic-like properties are able to restore mechanical damages by crack healing similarly to a biological healing process. In other words, at relatively high temperatures, the outward diffusion of A-element from MAX phases could heal millimeter-sized cracks through the formation of intermediate solid phases resulting from the oxidation of the diffused A-element. Ti2SnC, as one of MAX phases, was successfully welded to Ti6Al4V (TC4) through Cu interlayer in Ar atmosphere at low temperature 750�ºC during 1h under an applied mechanical pressure 10MPa. Until now, this adopted temperature is lowest in the published diffusion bonding work of MAX phases. The results indicated that the outward diffusion of Sn from Ti2SnC played a critical role in the chemical composition of joints. With the increasing processing time, Sn atoms migrated and accumulated adjacent to TC4 side as diffusion of Ti into Cu-Sn is effective to decrease the activity of Sn. After 60 mins, the reaction layers consisted of five zones: interleaved �²-Cu(Sn) and �±-Cu(Sn) zone zone (V), enriched Sn and CuTi0.5Sn0.5 intermetallic phase (IV), poor Sn, Ti and rich Cu zone (III), Ti3Cu4 intermetallic (II) and �²-Ti (Cu) phase (I). Shear test results showed that the average shear strength reached 85.7�±10 MPa. Corresponding fractographs indicated that the crack mainly propagated along Ti2SnC substrate adjacent to the bonding zone, accompanied with an intergranular fracture mode.

Biography :

Wenbo Yu has completed his PhD from Universite de Poitiers and did Post-doctoral studies in Tsinghua University School of Material Science and Engineering. He has published more than 9 papers in reputed journals. He mainly works on MAX phases and SiCf reinforced composite.

Email: wenboyu@mail.tsinghua.edu.cn

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward