alexa Manufacturing Of Gasket Sheet Using Paper Manufacturing Process Without Organic Solvent
ISSN: 2169-0022

Journal of Material Sciences & Engineering
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Share This Page

Additional Info

Loading
Loading Please wait..
 

9th World Congress on Materials Science and Engineering
June 12-14, 2017 Rome, Italy

Yoonjong Yoo, Hyejeong Lee, Minchul Ha, Seongki Kim and Sanghoon Lee
Korea Institute of Energy Research, Republic of Korea
JEIL E&S Co. Ltd., Republic of Korea
Posters & Accepted Abstracts: J Material Sci Eng
DOI: 10.4172/2169-0022-C1-068
Abstract
This paper is about ceramic gasket manufacturing technology that can be used in extreme temperatures. This gasket is manufactured using ceramic fiber and talc as main raw materials, and inorganic content is about more than 95 percent. Therefore, gasket has thermal stability, chemical and corrosion resistance and superior properties. So the chemical plant, high pressure thermal processing, streamlines and can be used. In this study, paper manufacturing method applied for preparation of the ceramic gasket sheet and its new economic process will be discussed. Inorganic fiber, talc and binders evenly distributed in the water for manufacture the gasket. Then dehydration on the wire mesh by supplying the slurry, and compression, through drying process completed the gasket for extreme temperature. The characteristics of manufactured product during the experiment like tare density was 1.88g/cm3, tensile strength was 0.15 kg/mm2, compressibility 39%, recovery 17% and ignition loss 6.55% at 1,000ºC. And there was no pressure drop when subjected to 150 LB (two inch) 10 kgf/cm2 nitrogen for 10 minutes. All the additives are being evenly distributed to the surface of the gasket, and each other's bonds have been completed successfully, and the applicability by paper manufacturing process. Solvent free gasket manufacturing process
1) All gasket materials such as water-based latex, mineral fiber and fillers are easily in water and evenly distributed.
2) Was dehydration a lot of influence on the size of the cohesion within the slurry in forming process.
3) An example a continuous process for a product is as follows: Mixture of raw materials→forming and dehydration→third stage compression→two stage drying → third stage calendering→rolling
4) New process is no odor is a clean work environment.
Acknowledgment
This subject is supported by Korea of Environmental Industry& Technology Institute(KEITI), Korea Ministry of Environment (MOE) as “Advancement ofEnvironmental IndustryTechnology DevelopmentProgram”(PN :1485013985)
Biography

Yoonjong Yoo's Major Research Fieldare Honeycomb adsorbents for VOC, CO2, humidity adsorption, Ceramic paper, Zeolite paper, Active carbon paper for adsorption materials, Carbon (chopped)fiber paper and mat for GDL and plane heater and Solvent free gasket manufacturing process for high temperature using. And working at Korea Institute of Energy Research(KIER).

Email: [email protected]

image PDF   |   image HTML
 

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords