alexa Multiferroic And Magnetoelectric Properties Of BCT-ZF Ceramics
ISSN: 2169-0022

Journal of Material Sciences & Engineering
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Share This Page

Additional Info

Loading
Loading Please wait..
 

3rd International Conference and Expo on Ceramics and Composite Materials
June 26-27, 2017 Madrid, Spain

Rashmi Rani, Radheshyam Rai, Seema Sharma, Madan Lal, Mamta Shandilya and Arpana Singh
Ecole Polytechnique, France
Shoolini University, India
A N College, Patna, India
ScientificTracks Abstracts: J Material Sci Eng
DOI: 10.4172/2169-0022-C1-070
Abstract
Multiferroic BCT-ZF ceramics were prepared from ferromagnetic (FM) zinc ferrite (ZF) and ferroelectric (FE) barium calcium titanate (BCT) with different mole % age of x, ((1-x)BaO.96CaO.O4TiO3–(x)ZnFe2O4) by using solid state reaction method. The preliminary structural studies were carried out by using x-ray diffraction technique, which confirm that the samples have a tetragonal structure along with the cubic spinel ferrite phase at room temperature with the average crystallite size of 22-32 nm. Raman spectra of these composites also confirm the existence of BCT phase and ZF phase respectively. Room temperature ferroelectric characterizations have shown that the samples are ferroelectric along with an adequate magnetoelectric coupling of 10.85 mV/(cm. Oe). The strong dependence of electric parameters on applied magnetic DC bias fields provides a framework for the development of potential magnetoelectric devices. Also, the high sensitivity of magnetoelectric coupling to the applied AC magnetic field can be used for its application in magnetoelectric sensors.
Biography

Rashmi Rani has completed PhD dual degree in Physics (from India and Italy) under the Erasmus Mundus (European Commission) scholarship in May 2015. She has experience in synthesis and the morphological, structural and electrical characterization of electro-ceramics and nanocrystalline ceramics for memory device applications. Further, she has also worked extensively on ferroelectric thin-films, polymers and metal oxide nano-fibers for biomedical applications and tissue engineering. The core area of her experimental expertise is in preparation of electro-ceramics by solid state reaction, sol-gel technology and hydrothermal method, Microwave Assisted Radiant Heating (MARH), thin films, spin coating technique, electrospinning and electrodeposition. Her experience in experimental techniques is as follows: XRD, TEM, SEM, TGA-DSC, Impedance Spectroscopy, LCR Meter, DC resistivity, FTIR, Raman analysis and UV-Vis spectroscopy. She has published 13 research papers in international refereed journals.

Email: [email protected]

image PDF   |   image HTML
 

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords