Synthesis Of NiCr-70Cr3C2 Nano-composites By High Energy Ball Milling And Their Morphological Characterization | 35003
ISSN: 2169-0022

Journal of Material Sciences & Engineering
Open Access

Our Group organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations
700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Synthesis of NiCr-70Cr3C2 nano-composites by high energy ball milling and their morphological characterization

4th International Conference and Exhibition on Materials Science & Engineering

Panta P C, Guaglianoni W C and Bergmann C P

Federal University of Rio Grande do Sul, Brazil

Posters-Accepted Abstracts: J Material Sci Eng

DOI: 10.4172/2169-0022.C1.029

Abstract
Nanostructured NiCr-70Cr3C2 powders were synthesized by high energy ball milling in a planetary ball mill. Two ball-to-powder ratios, four milling times and two milling speeds were used. The material was characterized by X-ray diffraction (crystalline phases and crystallite size), particle size analysis (average grain diameter), and scanning electron microscopy (powder morphology). With the increasing BPR, milling time and speed the crystallite size and mean diameter decreases. The result shows that using a ballto- powder weight ratio of 1:20, a milling time of 1 h and a milling speed of 500 rpm, the average particle size and crystallite size were, respectively, 5.6 μm and 8.3 nm.
Biography

Panta P C is Postdoctoral student in the Department of Materials Engineering at the Federal University of Rio Grande do Sul, Brazil.