alexa Adsorption of Cu and Mn on covalently cross-linked alginate gel beads.
Chemistry

Chemistry

Chemical Sciences Journal

Author(s): Gotoh T, Matsushima K, Kikuchi K

Abstract Share this page

Abstract The covalently cross-linked alginate gel beads were prepared by the reactions of Ca(2+)-doped alginate gel beads, which were formed by spraying a viscous alginate solution into a calcium chloride solution, with cyanogen bromide and following 1,6-diaminohexane. The cross-linking of alginate matrix decreased the mean bead diameter by about 30\% and made the beads durable in some extent under alkaline conditions. The adsorption of metal ions on the covalently cross-linked alginate gel beads was rapid and reached at equilibrium within 30 min at 25 degrees C. Adsorption isotherms of Cu(II), Mn(II), and Ca2+ on the beads possessed a stepwise shape, which was firstly determined by Rorrer et al. [Ind. Eng. Chem. Res. 32 (1993) 2170] for cross-linked chitosan gel beads and explained by a pore-blockage mechanism. Higher selectivity was determined against Cu(II) over Mn(II) and Ca2+, especially at a low concentration region. These metal adsorption profiles for the covalently cross-linked alginate gel beads was almost the same as those for the un-cross-linked beads, indicating that the cross-linking reactions were performed without interfering the adsorption characteristics of alginate gel beads.
This article was published in Chemosphere and referenced in Chemical Sciences Journal

Relevant Expert PPTs

Recommended Conferences

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords