alexa Age-hardening associated with grain boundary precipitation in a commercial dental gold alloy.
Engineering

Engineering

Journal of Steel Structures & Construction

Author(s): Kim HI, Jang MI, Kim MS

Abstract Share this page

Abstract The aim of this study was to make clear the age-hardening mechanism in a dental high carat gold alloy. For this purpose, age-hardening behaviour of a commercial dental high carat gold alloy, 65.5 wt\% Au-14.0 wt\% Ag-10.0 wt\% Cu-8.9 wt\% Pt, was investigated by means of hardness testing, X-ray diffraction study and scanning electron microscopy. Age-hardening was generated by the coherency strain resulting from the transformation of the alpha single phase to the Ag-rich alpha 1 phase and the AuCu I type ordered phase. The coherency strain seemed to be associated with the nucleation of the AuCu ordered structure initially, and then was brought about with the simultaneous formation of the Ag-rich alpha 1 phase and the AuCu I type ordered phase. Hardening was attributed mainly to the very fine coherent precipitates of a lamellar structure composed of the Ag-rich alpha 1 phase and the AuCu I type ordered phase at grain boundaries, and softening, which occurred following prolonged ageing, was due to the coarsening of the fine lamellar structure by releasing the strain at the interfaces of the adjacent lamellae.
This article was published in J Oral Rehabil and referenced in Journal of Steel Structures & Construction

Relevant Expert PPTs

Recommended Conferences

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords