alexa Characterization of set Intermediate Restorative Material, Biodentine, Bioaggregate and a prototype calcium silicate cement for use as root-end filling materials.
Dentistry

Dentistry

Journal of Oral Hygiene & Health

Author(s): Grech L, Mallia B, Camilleri J

Abstract Share this page

Abstract AIM: To investigate the composition of materials and leachate of a hydrated prototype cement composed of tricalcium silicate and radiopacifier and compare this to other tricalcium silicate-based cements (Biodentine and Bioaggregate) to assess whether the additives in the proprietary brand cements affect the hydration of the materials, using Intermediate Restorative Material (IRM), a standard root-end filling material as a control. METHODOLOGY: The materials investigated included a prototype-radiopacified tricalcium silicate cement, Biodentine, Bioaggregate and Intermediate Restorative Material (IRM). The pH and calcium ion concentration of the leachate were investigated. The hydrated cements were characterized using scanning electron microscopy (SEM) and X-ray energy dispersive analysis (EDX), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). RESULTS: All the cements tested were alkaline. The tricalcium silicate-based cements leached calcium in solution. Scanning electron microscopy of the prototype-radiopacified tricalcium silicate cement, Biodentine and Bioaggregate displayed hydrating cement grains, surrounded by a matrix composed of calcium silicate hydrate and calcium hydroxide. The presence of calcium hydroxide was evident from the XRD plots. FT-IR indicated the occurrence of a poorly crystalline calcium silicate hydrate. Biodentine displayed the presence of calcium carbonate. Bioaggregate incorporated a phosphate-containing phase. IRM consisted of zinc oxide interspersed in an organic matrix. CONCLUSIONS: The hydration of prototype-radiopacified tricalcium silicate cement, Biodentine and Bioaggregate resulted in the formation of calcium silicate hydrate and calcium hydroxide, which was leached in solution. The hydrated materials were composed of a cementitous phase that was rich in calcium and silicon and a radiopacifying material. Biodentine included calcium carbonate, and Bioaggregate included silica and calcium phosphate in the powders. IRM was composed of zinc oxide interspersed in a matrix of organic material. © 2012 International Endodontic Journal. Published by John Wiley & Sons Ltd. This article was published in Int Endod J and referenced in Journal of Oral Hygiene & Health

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords