alexa Chemical and microstructural characterization studies on natural and heat treated brannerite samples
Chemical Engineering

Chemical Engineering

Journal of Chemical Engineering & Process Technology

Author(s): F Charalambous, Rajeshwar Ram, Mark I Pownceby, Suresh Bhargava

Abstract Share this page

Two naturally occurring brannerite samples from the Crockers Well and Roxby Downs deposits in South Australia were characterised to assess their compositional, mineralogical, and textural properties. Characterisation was undertaken using X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Raman Spectroscopy and an Electron Probe Micro-analysis (EPMA). The samples were also heat treated to examine the effect of temperature on recrystallisation, mineral stability and deportment of impurities. In each sample, the brannerite was found to be thorium-rich (similar to 8-10 wt.% Th) indicating partial solid solution between brannerite and thorutite (ThTi2O6). Other minerals identified in the samples were thorutite (ThTi2O6), uranothorite ([Th, U]SiO4), a thorianite-uraninite solid solution ([Th, U]O-2) and gangue minerals including rutile, quartz, aluminosilicates, zircon, titanite, apatite and unidentified REE-containing phosphates. The brannerite in both samples was amorphous having undergone radiation-induced metamictisation. Crystallinity of the brannerite was restored upon heating of the samples to 1200 degrees C for 24 h in air. For the Crockers Well sample, radiation damage annealing/recrystallisation began at temperatures as low as 800 degrees C while the Roxby Downs sample did not begin to show evidence for recrystallisation until 900 degrees C. The main mineralogical changes after heating and recrystallisation involved a decrease in the amount of thorianite-uraninite phase due to decomposition into ThO2 and UO2 as well as the formation of Pb-rich glass films at grain boundaries. Compositional, textural and microstructural aspects of brannerite are likely to play an important role in any process to extract uranium from brannerite-containing ores. Discover the world's research

This article was published in Minerals Engineering and referenced in Journal of Chemical Engineering & Process Technology

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Peer Reviewed Journals
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version