alexa Compatibility of machined Ce-TZP Al2O3 nanocomposite and a veneering ceramic.

Author(s): Fischer J, Stawarczyk B

Abstract Share this page

Abstract OBJECTIVES: Due to its high fracture toughness ceria-stabilized ZrO(2)/Al(2)O(3) nanocomposite (Ce-TZP/A) could be superior to Y-TZP in clinical use. However, the compatibility to veneering ceramics is not yet investigated and therefore subject of this study. METHODS: Fracture strength and crazing resistance of veneered Ce-TZP/A frameworks (Nanozir, Matsushita Electric Works) were investigated in comparison to sintered and hipped Y-TZP (Hint-ELs). Frameworks were machined (HiCut, Hint-ELs), sintered where applicable (hiTherm, Hint-ELs), and veneered in a standardized procedure (Cerabien ZR, Noritake). Fracture strength of the crowns was assessed in a shear test (n=10). Biaxial flexural strength of the core materials was measured according to ISO 6872 (n=10). To assess the thermal compatibility between framework and veneer the coefficient of thermal expansion (CTE) of all materials was determined (n=3) and a crazing test carried out (n=12). RESULTS: Fracture strength was equal for crowns with Ce-TZP/A (866.6+/-132.1N) and sintered Y-TZP (904.5+/-168.2N), while crowns with hipped Y-TZP were significantly stronger (1380.6+/-253.2N) (Student's t-test, p<0.05). These values correlated with the biaxial flexural strength of the three core materials (Ce-TZP/A: 1238.0+/-200.0MPa, sintered Y-TZP: 1181.8+/-232.5MPa and hipped Y-TZP: 1521.8+/-163.8MPa). Failure of both hipped and sintered Y-TZP crowns occurred by chipping of the veneer or total fracture, while the Ce-TZP/A crowns predominantly failed by chipping of the veneer. In the crazing test both sintered and hipped Y-TZP performed slightly better than Ce-TZP/A. CTE's were as follows: Ce-TZP/A: 10.3microm/mK, sintered Y-TZP: 10.7microm/mK, hipped Y-TZP: 10.9microm/mK, and Cerabien ZR: 9.9microm/mK. SIGNIFICANCE: The CTE of the veneering ceramic has to be adjusted to Ce-TZP/A frameworks. This article was published in Dent Mater and referenced in

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Recommended Journals

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords