alexa Effect of acidic environment on the push-out bond strength of mineral trioxide aggregate.


Journal of Oral Hygiene & Health

Author(s): Shokouhinejad N, Nekoofar MH, Iravani A, Kharrazifard MJ, Dummer PM

Abstract Share this page

Abstract INTRODUCTION: Reduced surface microhardness and decreased sealing ability have been shown after the placement of mineral trioxide aggregate (MTA) in an acidic environment. In this study, the effect of an acidic environment on the push-out strength of MTA was evaluated. METHODS: Eighty root dentin slices from freshly extracted single-rooted human teeth were sectioned and their lumen instrumented to achieve a diameter of 1.3 mm. One gram of tooth-colored ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN) was mixed with 0.33 g of distilled water and introduced into the canals of the root-dentin slices and treated with ultrasonic energy. The specimens were then randomly divided into four groups (n = 20) and wrapped in pieces of gauze soaked in phosphate buffer saline solution (pH = 7.4) and butyric acid buffered at pH values of 4.4, 5.4, or 6.4, respectively. They were then incubated for 4 days at 37 degrees C. The push-out bond strengths were then measured using a universal testing machine. The slices were examined under a light microscope at x40 magnification to determine the nature of the bond failure. The data were analyzed using one-way analysis of variance and the Tamhane post hoc test. RESULTS: The greatest mean push-out bond strength (7.28 +/- 2.28 MPa) was observed after exposure to a pH value of 7.4. The values decreased to 2.47 +/- 0.61 MPa after exposure to a pH value of 4.4. There were significant differences between the groups (p < 0.001). Inspection of the samples revealed the bond failure to be predominantly adhesive. CONCLUSION: The force needed for displacement of MTA was significantly lower in samples stored at lower pH values. Copyright (c) 2010 American Association of Endodontists. All rights reserved. This article was published in J Endod and referenced in Journal of Oral Hygiene & Health

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

OMICS International Journals
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

Agri, Food, Aqua and Veterinary Science Journals

Dr. Krish

1-702-714-7001 Extn: 9040

Clinical and Biochemistry Journals

Datta A

1-702-714-7001Extn: 9037

Business & Management Journals


1-702-714-7001Extn: 9042

Chemical Engineering and Chemistry Journals

Gabriel Shaw

1-702-714-7001 Extn: 9040

Earth & Environmental Sciences

Katie Wilson

1-702-714-7001Extn: 9042

Engineering Journals

James Franklin

1-702-714-7001Extn: 9042

General Science and Health care Journals

Andrea Jason

1-702-714-7001Extn: 9043

Genetics and Molecular Biology Journals

Anna Melissa

1-702-714-7001 Extn: 9006

Immunology & Microbiology Journals

David Gorantl

1-702-714-7001Extn: 9014

Informatics Journals

Stephanie Skinner

1-702-714-7001Extn: 9039

Material Sciences Journals

Rachle Green

1-702-714-7001Extn: 9039

Mathematics and Physics Journals

Jim Willison

1-702-714-7001 Extn: 9042

Medical Journals

Nimmi Anna

1-702-714-7001 Extn: 9038

Neuroscience & Psychology Journals

Nathan T

1-702-714-7001Extn: 9041

Pharmaceutical Sciences Journals

John Behannon

1-702-714-7001Extn: 9007

Social & Political Science Journals

Steve Harry

1-702-714-7001 Extn: 9042

© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version