Author(s): Ye X, Wang L, Tse ZT, Tang G, Song G
Abstract Share this page
Abstract The effect of electro-pulsing treatment (EPT) on the microstructure, mechanical properties and corrosion behavior of cold-rolled Ti-6Al-4V alloy strips was investigated in this paper. It was found that the elongation to failure of materials obtains a noticeable enhancement with increased EPT processing time while slightly sacrificing strength. Fine recrystallized grains and the relative highest elongation to failure (32.5\%) appear in the 11second-EPT samples. Grain coarsening and decreased ductility were brought in with longer EPT duration time. Fracture surface analysis shows that transition from intergranular brittle facture to transgranular dimple fracture takes place with an increase in processing time of EPT. Meanwhile, corrosion behavior of titanium alloys is greatly improved with increased EPT processing time, which is presented by polarization test and surface observation with the beneficial effect of forming a protective anatase-TiO2 film on the surface of alloys. The rapid recrystallization behavior and oxide formation of the titanium alloy strip under EPTs are attributed to the enhancement of nucleation rate, atomic diffusion and oxygen migration resulting from the coupling of the thermal and athermal effects. Copyright © 2015 Elsevier B.V. All rights reserved.
This article was published in Mater Sci Eng C Mater Biol Appl
and referenced in Journal of Material Sciences & Engineering