alexa Ex vivo surface and mechanical properties of coated orthodontic archwires.


Journal of Oral Hygiene & Health

Author(s): Elayyan F, Silikas N, Bearn D

Abstract Share this page

Abstract This study examined the mechanical and physical properties of retrieved coated nickel-titanium (NiTi) archwires compared with unused samples. Ultraesthetic 0.016 inch coated archwires (G&H(R) Wire Company) were investigated. Ten as-received wires were subjected to a three-point bending test using conventional and self-ligating bracket systems. Surface roughness of the coating was measured with a contact stylus profilometer. Optical and scanning electron microscopes were used to assess surface topography. Ten archwires were used in vivo for a period of between 4 and 6 weeks. Retrieved archwires were subjected to the same tests. The percentage of the remaining coating was calculated using digital photography. Coated archwires were used in vivo for a mean period of 33 days. Differences between the mean values of the as-received and retrieved archwires were determined using t-tests. In the three-point bending test, with conventional elastomeric ligation, retrieved wires produced a lower unloading force (P < 0.001). Both retrieved and as-received coated archwires produced zero values of unloading force when deflected for 4 mm. When tested using a self-ligating bracket system, retrieved and as-received coated archwires produced the same amount of force (P > 0.05). With surface profilometry, all measured roughness parameters (except R(sm)) had greater surface roughness for the retrieved coated archwires (P < 0.05). Under microscopy, retrieved coated archwires showed discolouration, ditching, and delamination. Only 75 per cent of the coating was present in retrieved coated archwires. Retrieved coated archwires produced lower unloading force values than as-received coated archwires with conventional ligation. Surface roughness of coated archwires increased after use. Coated archwires have a low aesthetic value, with 25 per cent of the coating lost within 33 days in vivo. This article was published in Eur J Orthod and referenced in Journal of Oral Hygiene & Health

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Peer Reviewed Journals
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version