Author(s): Grech L, Mallia B, Camilleri J
Abstract Share this page
Abstract OBJECTIVE: Tricalcium silicate-based cements have been displayed as suitable root-end filling materials. The physical properties of prototype radiopacified tricalcium silicate cement, Bioaggregate and Biodentine were investigated. Intermediate restorative material was used as a control. METHODS: The physical properties of a prototype zirconium oxide replaced tricalcium silicate cement and two proprietary cements composed of tricalcium silicate namely Bioaggregate and Biodentine were investigated. Intermediate restorative material (IRM) was used as a control. Radiopacity assessment was undertaken and expressed in thickness of aluminum. In addition the anti-washout resistance was investigated using a novel basket-drop method and the fluid uptake, sorption and solubility were investigated using a gravimetric method. The setting time was assessed using an indentation technique and compressive strength and micro-hardness of the test materials were investigated. All the testing was performed with the test materials immersed in Hank's balanced salt solution. RESULTS: All the materials tested had a radiopacity value higher than 3mm thickness of aluminum. IRM exhibited the highest radiopacity. Biodentine demonstrated a high washout, low fluid uptake and sorption values, low setting time and superior mechanical properties. The fluid uptake and setting time was the highest for Bioaggregate. SIGNIFICANCE: The addition of admixtures to tricalcium silicate-based cements affects the physical properties of the materials. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
This article was published in Dent Mater
and referenced in Journal of Oral Hygiene & Health