alexa Low viscosity hydrogel of guar gum: preparation and physicochemical characterization.
Chemical Engineering

Chemical Engineering

Journal of Analytical & Bioanalytical Techniques

Author(s): Cunha PL, Castro RR, Rocha FA, de Paula RC, Feitosa JP

Abstract Share this page

Abstract Guar gum was cross-linked with glutaraldehyde and characterized by GPC, rheology, WADX, SEM and TGA. This guar gum is a galactomannan polysaccharide, that contains small amount of arabinose, glucose and uronic acid, besides galactose and mannose. The polymer has high molar mass, with Mw, Mn and Mv values of 2.0x10(6), 1.2x10(6) and 1.9x10(6)g/mol, respectively. The reticulation follows a slow process and lead to a viscosity increase of 40 times compared with the original gum solution. The final viscosity was similar to that of Hylan G-F 20, a hyaluronate derivative, commercially used in viscosupplementation treatment. The gel contains 95.6\% of water and the amount of residual glutaraldehyde is much lower than the LD-50. Porous structure was detected by SEM and thermal stability was improved by the cross-linking. The low viscosity, the small amount of remained glutaraldehyde, and the thermal stability indicates that the guar hydrogel has potential to be applied as biomaterial with specific rheological requirements. This article was published in Int J Biol Macromol and referenced in Journal of Analytical & Bioanalytical Techniques

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords