alexa Nanocrystalline tetracalcium phosphate cement.
Engineering

Engineering

Bioceramics Development and Applications

Author(s): Gbureck U, Barralet JE, Hofmann MP, Thul R

Abstract Share this page

Abstract Calcium hydroxide cements can lack long-term stability and achieve sustained release by matrix-controlled diffusion of hydroxyl ions. Tetracalcium phosphate (TTCP) hydrolyzes slowly to form calcium hydroxide and a thin insoluble apatite layer that prevents further reaction. In this study, mechanical amorphization was used to create a setting calcium-hydroxide-releasing cement from TTCP. The effect of high-energy ball milling of TTCP on the mechanical properties of the cement was investigated. X-ray diffraction data were used to determine the phase composition of the set cements. An accelerated in vitro test compared pH of water after prolonged boiling of nanocrystalline TTCP cements and a calcium salicylate material. As milling time increased, cement compressive strength and degree of conversion increased. Hydroxyl ion release from the cement was comparable with that from a calcium salicylate material. This new cement system offers the antimicrobial potential of calcium salicylate materials combined with the long-term stability of insoluble apatite cements.
This article was published in J Dent Res and referenced in Bioceramics Development and Applications

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords