alexa Pore size control for mesoporous titanium hydroxide prepared with mixed template molecules and its fluoride ion exchange property
Chemical Engineering

Chemical Engineering

Journal of Analytical & Bioanalytical Techniques

Author(s): Tatsumi Ishihara, Yuko Misumi, Hiroshige Matsumoto

Abstract Share this page

Control of pore size on mesoporous titanium hydroxide denoted as TiOX(OH)2+δ with zirconium additive was studied by using different size template molecules. The mesopore diameter of TiOX(OH)2+δ increased monotonically with increasing size of the organic template molecule used. The use of a mixture of template molecules with different size allowed for accurate pore size control of TiOX(OH)2+δ. Moreover, a pore size between those of single template molecules was obtained using a mixture of two different template molecules. The fluoride ion exchange capacity of Zr-added TiOX(OH)2+δ also increased with increasing mesopore diameter, and the largest fluoride ion exchange capacity was achieved on the sample with 3.34 nm pore size, and the fluoride ion exchange capacity was further improved by the accurate control of pore size. The amount of fluoride ions adsorbed was 1.1 mmol/g against 50 ppm NaF solution; this was observed in TiOX(OH)2+δ with 4.2 nm pore size, which was obtained using a 3:1 mixture of C12H25NH2:C14H29NH2 as the template molecule.

This article was published in Microporous and Mesoporous Materials and referenced in Journal of Analytical & Bioanalytical Techniques

Relevant Expert PPTs

Relevant Speaker PPTs

Recommended Conferences

Relevant Topics

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords