alexa Shear bond strength of metallic brackets photo-activated with light-emitting diode (LED) at different exposure times.



Author(s): Rgo EB, Romano FL

Abstract Share this page

Abstract The purpose of this study was to compare the shear bond strength of orthodontic metallic brackets photo-activated with two different light-curing sources at different exposure times: halogen light (XL 1500, 3M ESPE) and LED light (Ortholux, 3M Unitek). Sixty bovine permanent lower incisors were inserted into PVC tubes containing plaster. The buccal surfaces were cleaned with pumice and water, and then etched with 37\% phosphoric acid gel. The XT Primer bonding agent (3M Unitek) was applied to the enamel surfaces and the metallic pre-coated brackets (Transbond APC II system, 3M Unitek) were attached to upper central incisors. The teeth were randomly divided into four groups (n=15). In Group I (Control), halogen light was used for 40 seconds, while in Groups II, III, and IV were light-cured with LED light unit for 40, 10, and 5 seconds, respectively. The teeth were stored in distilled water at 37 degrees C for 24 hours. The brackets were submitted to shear bond strength test in universal testing machine (Instron) at a crosshead speed of 0.5 mm/minute. Shear bond strength means (MPa) were 4.87 for Group I; 5.89 for Group II; 4.83 for Group III, and 4.39 for Group IV. Tukey's test detected no statistically significant differences among the groups regarding the shear bond strength (p>0.05). Neither of the types of light-curing sources or exposure times influenced the shear bond strength of metallic brackets.
This article was published in J Appl Oral Sci and referenced in Dentistry

Relevant Expert PPTs

Recommended Conferences

Relevant Topics

Peer Reviewed Journals
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version