alexa Synthesis and characterization of TiO2nanopowders from peroxotitanium solutions.
Materials Science

Materials Science

Research & Reviews: Journal of Material Sciences

Author(s): Jianshu Lu, Luciana Pitta Bauermann, Peter Gerstel, Ute Heinrichs, Peter Kopold

Abstract Share this page

TiO2 nanopowders have been synthesized from a peroxotitanium solution chemical bath route. The variation of H+ concentrations of the reaction solutions was measured during the course of the synthesis. X-ray diffraction analysis and transmission electron microscope observation showed that peroxotitanium concentration can affect the crystal type and morphology of the TiO2 nanopowders. The particle size of TiO2 nanopowders prepared from 0.1 mol L−1 peroxotitanium is 7.7 nm. The specific surface area of this nanopowder is 250 m2 g−1. Thermogravimetric analysis showed that the TiO2 nanopowder dried at 80 °C for 24 h contains 11% water.

This article was published in Mater ChemPhys and referenced in Research & Reviews: Journal of Material Sciences

Relevant Expert PPTs

Relevant Speaker PPTs

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords