alexa The effect of PEGT PBT scaffold architecture on the composition of tissue engineered cartilage.


Journal of Biomimetics Biomaterials and Tissue Engineering

Author(s): Malda J, Woodfield TB, van der Vloodt F, Wilson C, Martens DE,

Abstract Share this page

Abstract A highly interconnecting and accessible pore network has been suggested as one of a number of prerequisites in the design of scaffolds for tissue engineering. In the present study, two processing techniques, compression-molding/particulate-leaching (CM), and 3D fiber deposition (3DF), were used to develop porous scaffolds from biodegradable poly(ethylene glycol)-terephthalate/poly(butylene terephthalate) (PEGT/PBT) co-polymers with varying pore architectures. Three-dimensional micro-computed tomography (microCT) was used to characterize scaffold architectures and scaffolds were seeded with articular chondrocytes to evaluate tissue formation. Scaffold porosity ranged between 75\% and 80\%. Average pore size of tortuous CM scaffolds (182 microm) was lower than those of organized 3DF scaffolds (525 microm). The weight ratio of glycosaminoglycans (GAG)/DNA, as a measure of cartilage-like tissue formation, did not change after 14 days of culture whereas, following subcutaneous implantation, GAG/DNA increased significantly and was significantly higher in 3DF constructs than in CM constructs, whilst collagen type II was present within both constructs. In conclusion, 3DF PEGT/PBT scaffolds create an environment in vivo that enhances cartilaginous matrix deposition and hold particular promise for treatment of articular cartilage defects. Copyright 2004 Elsevier Ltd. This article was published in Biomaterials and referenced in Journal of Biomimetics Biomaterials and Tissue Engineering

Relevant Expert PPTs

Relevant Speaker PPTs

Peer Reviewed Journals
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version