Author(s): Gao J, Chen R, Li DH, Jiang L, Ye JC,
Abstract Share this page
Abstract Multifunctional single crystalline tin-doped indium oxide (ITO) nanowires with tuned Sn doping levels are synthesized via a vapor transport method. The Sn concentration in the nanowires can reach 6.4 at.\% at a synthesis temperature of 840 °C, significantly exceeding the Sn solubility in ITO bulks grown at comparable temperatures, which we attribute to the unique feature of the vapor-liquid-solid growth. As a promising transparent conducting oxide nanomaterial, layers of these ITO nanowires exhibit a sheet resistance as low as 6.4 Ω/[Symbol: see text] and measurements on individual nanowires give a resistivity of 2.4 × 10(-4) Ω cm with an electron density up to 2.6 × 10(20) cm(-3), while the optical transmittance in the visible regime can reach ∼ 80\%. Under the ultraviolet excitation the ITO nanowire samples emit blue light, which can be ascribed to transitions related to defect levels. Furthermore, a room temperature ultraviolet light emission is observed in these ITO nanowires for the first time, and the exciton-related radiative process is identified by using temperature-dependent photoluminescence measurements.
This article was published in Nanotechnology
and referenced in Journal of Nanomedicine & Nanotechnology