alexa Abstract | Dielectric behavior and A. C. Conductivity in Cu-Ti Ferrites

Advances in Applied Science Research
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

Dielectric properties such as dielectric constant (Î’) and dielectric loss tangent were studied as a function of composition, frequency and temperature for a series of Cu1+XTixFe2-2xO4 ferrite samples prepared by using conventional ceramic technique. Initial Ti4+ ion substitution results in decrease in dielectric constant while dc resistivity increases on substitution. The measurement of dielectric constant with frequency (100Hz-1MHz) shows decrease in dielectric constant with increasing frequency and tends to reach constant value. Variation of dielectric constant with frequency at different temperature show increase in dielectric constant in general and the tendency of dispersion in dielectric constant observed increase with temperature. The variation of dielectric constant with temperature at different frequencies was studied. Dielectric constant steadily increases reaches to maximum and thereafter decreases. The frequency dependence of dielectric loss tangent is found to be abnormal for some samples. The frequency dependence of dielectric loss tangent at various temperatures was studied, the abnormal behavior of dielectric relaxation processes was observed. A.C. Conductivity was derived from dielectric constant and loss tangent data. The conduction in this system is interpreted as due to small polaron hopping.

To read the full article Peer-reviewed Article PDF image

Author(s): S C Chaudhari and R N Patil

Keywords

ferrite, loss tangent, dielectric constant, polaron hopping., polaron hopping

 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords