alexa Abstract | Effect of dip time on the structural, electrical and morphological properties of antimony sulphide thin films

Advances in Applied Science Research
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

Amorphous Sb2S3 thin films were deposited on glass substrates by solution growth technique. The structural property was analyzed by XRD, the elemental composition was estimated from EDX analysis while the surface morphology of the film was examined by SEM. The effect of dip time on each of these properties was studied. Amorphous nature of the film was confirmed from XRD and SEM analysis. The thickness of the Sb2S3 thin film was estimated from surface profile analysis and found to increase as deposition time increases. The resistance of the films at different dip time was obtained from V/I values from surface profile analysis. The film was seen to have very high resistance in the range of 1.23 x 109Ω to 1.29 x 109Ω while the sheet resistance was in the range of 0.645 x 103Ω-m to 1.23 x 103Ω-m depending on the dip time.

To read the full article Peer-reviewed Article PDF image

Author(s): M D Jeroh and D N Okoli

Keywords

Thin films, antimony sulphide, scanning electron microscopy, Surface profile, surface morphology, dip time, solution growth technique, amorphous., antimony sulphide

 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords