alexa Abstract | Effect of sintering temperature on structural, electrical, magnetic hysteresis and magnetoelectric effect on (x) Ni0.7Zn0.3Fe2O4 + (1-x) PLZT composite by Co-precipitation method

Advances in Applied Science Research
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

Magnetoelectric composites containing Ni0.7Zn0.3Fe2O4 and Pb0.93La0.07(Zr0.60Ti0.40)O3 phases have been prepared by chemical co-precipitation method. The structure and morphology of the composites were examined by means of X-ray diffraction (XRD) and scanning electron microscopic (SEM) The XRD result showed that the composites consisted of spinel Ni0.7Zn0.3Fe2O4 and perovskite PLZT annealing at temperature higher than 700 oC. The average grain size for the piezoelectric phase of the composite was found to increase the overall dielectric and ferroelectric property of the composite increased with increasing in sintering temperature. Variation of dielectric constant (ε) and dielectric loss (tanδ) with frequency for 0.30NZFO + 0.70PLZT composite with annealed at different temperature showed dispersion in the low frequency range. The variation of dielectric constant with temperature reflects DPT type behaviour. The dielectric properties are strongly influenced by interface phenomena (Maxwell- Wagner) due to the local electrical inhomgeneity. At low frequency range, the composite showed the dielectric dispersion is associated with very high polarization. The peak value of dielectric constant for composite decreased with increasing its sintering temperature. coercivity, saturation magnetization and squareeness have been found to vary with concentration of ferrite phase and annealing temperature due to the increase in crystallite size. The maximum value of the magnetoelectric conversion factor (dE/dH)max equal to 5.2 mV/cm*Oe is observed for 30%NZFO – 70% PLZT composites when sintered at 1100 oC.

To read the full article Peer-reviewed Article PDF image

Author(s): Abdul Samee Fawzi

Keywords

Composites, X-ray diffraction, Scanning electron microscopy, Dielectric properties, Magnetic properties, magnetoelectric effect., Scanning electron microscopy.

 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords