alexa Abstract | Thickness-dependent structural properties of chemically deposited Bi2S3 thin films

Advances in Applied Science Research
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

Thin films of Bi2S3 have been prepared by chemical bath deposition method using Bismuth nitrate and Sodium thiosulphate. Films were deposited onto well cleaned glass substrates with different bath temperatures. The effect of bath temperature on thickness was studied. The thickness goes on increasing with bath temperature reaches to maximum at 600C and decreases further increases in temperature after 600C. The good quality of film is obtained at 600C. The X-ray diffraction pattern revealed that bismuth sulphide thin films exhibit orthorhombic structure with polycrystalline in nature. The structural parameters (grain size 25-358Å, dislocation density 0.7789-159.57X1015 l/m2 and strain (ε) 14.61-1.027X10-3) have been calculated. Grain size increases with film thickness but the strain and dislocation density decreases. The films are oriented in (330) direction.

To read the full article Peer-reviewed Article PDF image

Author(s): V Balasubramanian N Suriyanarayanan S Prabahar

Keywords

Bismuth sulphide, Chemical bath deposition, Structural properties, Thin films, Chemical bath deposition

 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords