alexa Abstract | Effects of Silica Morphology on Emulsion Paint Properties Using Rice Husk Ash and Silica Flour as Pigment Extenders
ISSN ONLINE(2319-8753)PRINT(2347-6710)

International Journal of Innovative Research in Science, Engineering and Technology
Open Access

Like us on: https://twitter.com/ijirset_r
OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

This study investigated the effects of silica (SiO2) morphology on emulsion paint properties by comparing the physical properties of emulsion paints produced with amorphous silica ( rice husk ash) with those of crystalline silica (silica flour) used as pigment extenders in the paint. Calcium carbonate was used as the reference standard in the study. Rice husk ash (RHA) was obtained by heating rice husks on a gas stove to obtain rice husk char which was subjected to controlled incineration in a muffle furnace at a temperature of 6500C and duration of 4hrs. The granular RHA obtained was ground to obtain powdery RHA of smaller particle size. The RHA powder, silica flour (SF) and CaCO3 were then sieved to obtain the same particle size range of 32-63microns (μm) used in the formulation of the emulsion paints. The extender levels in the formulations were varied from 2-12% by weight and the physical properties of the emulsion paint variants were determined. The results revealed that RHA-filled white emulsion paints (RHAWEP) had higher viscosities than those of silica flour due to the amorphous nature of silica in RHA which conferred on it, a thickening effect superior to that of crystalline silica. RHAWEPs had higher pigment volume concentration (PVC) values than those of silica flour and CaCO3 due to its lower specific gravity and this resulted in the flat (non-glossy) appearance of the RHAWEP dry films but semi-gloss appearance of those of SF and CaCO3.

To read the full article Peer-reviewed Article PDF image

Author(s): Igwebike-Ossi, Clementina Dilim

Keywords

emulsion paint, rice husk ash (RHA), silica flour (SF), pigment extender, amorphous and crystalline silica, morphology, fluid dynamics

Share This Page

Additional Info

Loading
Loading Please wait..
 
 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords