alexa Abstract | Thermal Properties of Polyurethane-Polyisocyanurate (PUR-PIR) Foams Modified with Tris(5-Hydroxypenthyl) Citrate
ISSN: 2090-4568

Journal of Advanced Chemical Engineering
Open Access

OMICS International organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations

700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)

Research Article Open Access

Abstract

New polyol (citrate) for the production of PUR-PIR foams was obtained. The hydroxyl number of the obtained compound is 496 mg KOH/g. The amount of water in the new compound was 0.98%. Due to this amount, the foam recipe does not need to be modified. The obtained foam series contain from 0.1 R to 0.5 R of the new compound. The T5% values were higher by about 50% for the foams examined under nitrogen. The foams showed similar T10% values under both atmospheres. The T20% were higher by around 15°C for foams heated in nitrogen. The difference in the T50% was circa 150°C and foams heated in oxygen registered better value. The foams showed slight decrease in the T5%, T10%, T20% and T50% values in both atmospheres, as well as a decrease in the softening temperatures, along with the increasing amount of the tris(5-hydroxypentyl) citrate compound in them. New compound is new product, doesn’t described in literature. It has good thermal properties as industrial polyols but it is cheaper. Foams with this product have good thermal properties and they may be used in the building industry for thermal insulation

To read the full article Peer-reviewed Article PDF image | Peer-reviewed Full Article image

Author(s): Joanna Liszkowska, Bogusław Czupryński and Joanna Paciorek-Sadowska

Keywords

Polyurethane foam, Citric acid, Pentane glycol, Thermal properties, TG, Chemical Technology,Cheminformatics,Corrosion,Inorganic Chemical Technology,Mass Transfer

Share This Page

Additional Info

Loading
Loading Please wait..
 
 
 
 
Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version
adwords