Fabrication and Characterization of Carbon Black and Phenol Formaldehyde Composites

Jakir Hossain, Mohammad Saiful Alam, Shujit Chandra Paul and Shafiul Islam*
Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Bangladesh
*Corresponding Author : Shafiul Islam, Assitant Professor, Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Bangladesh, Tel: +8801725346333, Email: shafiulacce@gmail.com

Received Date: Feb 27, 2018 / Accepted Date: May 28, 2018 / Published Date: Jun 02, 2018

Abstract

Carbon black and Phenol formaldehyde composites were prepared by hot press molding at different temperature (180°C, 200°C, 220°C); pressure (100 kN, 150 kN, 200 kN, 250 kN); heating time (10 min, 20 min, 30 min, 60 min) and several compositions (50%C, 60%C, 70%C, 80%C, 90%C). The different properties such as physical, mechanical, thermal properties were studied by Universal Testing Machine (UTM), Micro hardness tester, TGA/DTA analyser and X-Ray diffractometer etc. In this work, it was observed that the bulk density was slightly changed for 50% carbon black and Phenol formaldehyde composites. Compressive strength of sample was increased with increasing the pressure, heating temperature and time.

Keywords: Carbon black; Phenol formaldehyde; Micro hardness