Our Group organises 3000+ Global Conferenceseries Events every year across USA, Europe & Asia with support from 1000 more scientific Societies and Publishes 700+ Open Access Journals which contains over 50000 eminent personalities, reputed scientists as editorial board members.

Open Access Journals gaining more Readers and Citations
700 Journals and 15,000,000 Readers Each Journal is getting 25,000+ Readers

This Readership is 10 times more when compared to other Subscription Journals (Source: Google Analytics)
Google Scholar citation report
Citations : 2154

Journal of Biotechnology & Biomaterials received 2154 citations as per Google Scholar report

Indexed In
  • Index Copernicus
  • Google Scholar
  • Sherpa Romeo
  • Open J Gate
  • Genamics JournalSeek
  • Academic Keys
  • ResearchBible
  • China National Knowledge Infrastructure (CNKI)
  • Access to Global Online Research in Agriculture (AGORA)
  • Electronic Journals Library
  • RefSeek
  • Hamdard University
  • EBSCO A-Z
  • OCLC- WorldCat
  • SWB online catalog
  • Virtual Library of Biology (vifabio)
  • Publons
  • Geneva Foundation for Medical Education and Research
  • Euro Pub
  • ICMJE
Recommended Journals
Share This Page

Formation and characterization of biomimetic calcium phosphate coatings on nanostructured surfaces of anodized titanium

2nd Annual Conference and Expo on BIOMATERIALS

Shaghayegh Javadi, Zahra Mohammadi and A S Mehdi Mesgar

Tehran University, Iran

Posters & Accepted Abstracts: J Biotechnol Biomater

DOI: 10.4172/2155-952X.C1.074

Abstract
Biomimetic coating procedure was used to deposit a bioactive layer of hydroxyapatite (HA) on the surface ��? modified titanium by anodization process. The anodization was performed on the clean surface of titanium under three different voltages of 80, 100 and 130v using HF as the electrolyte. The morphology, structure and topography of the anodized substrates were evaluated by Scaning Electron Microscopy (SEM) or Field Emission Scanning Electron Microscopy (FE-SEM), X ray Diffraction (XRD) and Atomic Force Microscopy (AFM), respectively. Biomimetic coatings were deposited on the surface of anodized titanium using a twostage procedure by immersion in two concentrated Simulated Body Fluids (SBF) with different concentration of Mg+2 and HCO3 -2 ions under physiological conditions. The results showed that an increase in anodization voltage tends to produce a porous surface with circular pores toward a columnar layer of rutile. The surface roughness of anodized surfaces was increased by increasing voltage. Biomimetic coating procedure was caused to form a HA layer which was proved by XRD, FTIR and SEM. The HA layer formed on the anodized titanium surface has a whisker-like morphology. The crystallinity of HA layer was increased by an increase in voltage. The findings indicate that the anodized titanium at high voltages may be suitable substrate for biomimetic coating procedure.
Biography

Shghayageh Javadi did her Master’s degree in Biomedical Engineering. Her thesis is about biomaterial coating and focused on best coating method of biomaterials. She has researched on different pretreatment for surface modification of titanium. She has used anodizing process with combination of alkali treatment for surface modification of titanium. The result of her search and experiments showed that the anodized titanium at high voltages may be suitable substrate for biomimetic coating procedure.